PA6/66
Glass Fiber Reinforced / Impact Modified
Glass fiber reinforced nylon for enhanced strength, stiffness and low temperature impact resistance.
C2201GT30BKE1
Material：
PA6/66
Specification：
Impact resistant 30% glass fiber reinforced
Color：
Black
Certification：
RoHS、REACH、GRS(Global Recycle Standard)
Package：
25kg
Property：
High stiffness, toughness and low temperature impact resistance, suitable for fabrication
1. Materials Standard:
| Test Items Property | Test Method | Unit | Vaule |
|---|---|---|---|
| Mechanical Properties | |||
| Tensile Strength | ASTM D638 | Kg/cm2 | 1300 |
| Elongation at Break | ASTM D638 | % | < 5 |
| Flexural Strength | ASTM D790 | kg/cm2 | 2050 |
| Flexural Modulus | ASTM D790 | kg/cm2 | 70000 |
|
IZOD Impact, Notched 1/8" 23°C IZOD Impact, Notched 1/8" -30°C |
ASTM D256 | kg-cm/cm |
16 |
|
Hardness Shore D Hardness Rockwell R Scale |
ASTM D2240 ASTM D785 |
- |
120 |
| Thermal | |||
|
Heat Deflection Temperature (18.6kg/cm2 ) |
ASTM D648 | °C | 245 |
| Other | |||
| Shrinkage | ASTM D955 | % | 0.3~0.8 |
| Melt Index | ASTM D1238 | g/10min | - |
| Specific Gravity | ASTM D792 | - | 1.33 |
| Ash Content | ASTM D482 | % | 30 |
| Equilibrium Moisture Content | ASTM D570 | % | < 0.3 |
| Flammability | UL 94 | 1.6mm | - |
2. Molding Condition:
| Drying | Melt Temp | Inject Press. |
|---|---|---|
| 80~100°C*4HR | 245~280°C | 20kg/cm2 |
Note: Test Conditions: 23℃, 50%RH, 24 hours. The datasheet is for your reference. And the data above will vary as the actual use condition changes.