PA6
Glass Fiber / Mineral Reinforced Grade
Glass fiber/mineral fiber reinforced nylon for increased strength, stiffness and surface improved.
RebornPlas Glass-Fiber Mineral Reinforced Nylon is great for automobile parts and industrail parts manufacture such as: headlight base, grinding wheel, and more.
A3000GM33BK
Material：
PA6
Specification：
33% glass fiber / mineral reinforcement
Color：
Black
Certification：
RoHS、REACH、GRS(Global Recycle Standard)
Package：
25kg
Property：
Excellent high stiffness, strength and surface improved
1. Materials Standard:
| Test Items Property | Test Method | Unit | Vaule |
|---|---|---|---|
| Mechanical Properties | |||
| Tensile Strength | ASTM D638 | Kg/cm2 | 1050 |
| Elongation at Break | ASTM D638 | % | < 5 |
| Flexural Strength | ASTM D790 | kg/cm2 | 1700 |
| Flexural Modulus | ASTM D790 | kg/cm2 | 62000 |
|
IZOD Impact, Notched 1/8" 23°C IZOD Impact, Notched 1/8" -30°C |
ASTM D256 | kg-cm/cm |
6 |
|
Hardness Shore D Hardness Rockwell R Scale |
ASTM D2240 ASTM D785 |
- |
115 |
| Thermal | |||
|
Heat Deflection Temperature (18.6kg/cm2 ) |
ASTM D648 | °C | 200 |
| Other | |||
| Shrinkage | ASTM D955 | % | 0.2~0.8 |
| Melt Index | ASTM D1238 | g/10min | - |
| Specific Gravity | ASTM D792 | - | 1.39 |
| Ash Content | ASTM D482 | % | 33 |
| Equilibrium Moisture Content | ASTM D570 | % | < 0.3 |
| Flammability | UL 94 | 1.6mm | - |
2. Molding Condition:
| Drying | Melt Temp | Inject Press. |
|---|---|---|
| 80~100°C*4HR | 235~260°C | 20kg/cm2 |
Note: Test Conditions: 23℃, 50%RH, 24 hours. The datasheet is for your reference. And the data above will vary as the actual use condition changes.