PA66
Flame Retardant Grade
Increase the flame resistance of nylon at high temperatures.
RebornPlas flame retardant nylon 66 is rated UL94 V0 ( 1 / 8"，1/ 16"，1 / 32"，1 / 64" thickness of specimens), it can increase the flame resistance of nylon at high temperatures. The burning will stop within 10 seconds on a vertical part, allows for drops of plastic that are not inflames.
This nylon is suitable for industrial parts and components producing, such as: Connector, Electrical switch housing, Power tools and more.
EB-V0
Material：
PA66
Specification：
UL94 V0 Rating
Color：
Natural color, providing custom dyeing service
Certification：
RoHS、REACH
Package：
25kg
Property：
High flame resistance and good formability
1. Materials Standard:
| Test Items Property | Test Method | Unit | Vaule |
|---|---|---|---|
| Mechanical Properties | |||
| Tensile Strength | ASTM D638 | Kg/cm2 | 700 |
| Elongation at Break | ASTM D638 | % | < 5 |
| Flexural Strength | ASTM D790 | kg/cm2 | 1300 |
| Flexural Modulus | ASTM D790 | kg/cm2 | 32000 |
|
IZOD Impact, Notched 1/8" 23°C IZOD Impact, Notched 1/8" -30°C |
ASTM D256 | kg-cm/cm |
3 |
|
Hardness Shore D Hardness Rockwell R Scale |
ASTM D2240 ASTM D785 |
- |
77 |
| Thermal | |||
|
Heat Deflection Temperature (18.6kg/cm2 ) |
ASTM D648 | °C | |
| Other | |||
| Shrinkage | ASTM D955 | % | 0.7~0.9 |
| Melt Index | ASTM D1238 | g/10min | - |
| Specific Gravity | ASTM D792 | - | 1.17 |
| Ash Content | ASTM D482 | % | - |
| Equilibrium Moisture Content | ASTM D570 | % | < 0.3 |
| Flammability | UL 94 | 1.6mm | V0 |
2. Molding Condition:
| Drying | Melt Temp | Inject Press. |
|---|---|---|
| 80~100°C*4HR | 245~280°C | 20kg/cm2 |
Note: Test Conditions: 23℃, 50%RH, 24 hours. The datasheet is for your reference. And the data above will vary as the actual use condition changes.