Ocean Plastic
Ultra Impact Modified Grade
Increase the toughness of nylon at low temperatures
Our ultra impact modified grade ocean plastic is a high-performance, sustainable material that is ideal for a wide range of applications. Made from recycled ocean plastic, it is modified to increase toughness at low temperatures.
This makes it ideal for demanding applications such as sports equipment, plugs, fan blades, plastic screws, gears, bicycle brake discs, and nuts.
A2000TBKA3
Material：
PA6
Specification：
Low Temperature Impact Resistance
Color：
Black
Certification：
RoHS、REACH、GRS、UL
Package：
25kg
Property：
Excellent high toughnesss, Low temperature impact resistance and surface improved
1. Materials Standard:
| Test Items Property | Test Method | Unit | Vaule |
|---|---|---|---|
| Mechanical Properties | |||
| Tensile Strength | ASTM D638 | Kg/cm2 | 430 |
| Elongation at Break | ASTM D638 | % | > 50 |
| Flexural Strength | ASTM D790 | kg/cm2 | 700 |
| Flexural Modulus | ASTM D790 | kg/cm2 | 17500 |
|
IZOD Impact, Notched 1/8" 23°C IZOD Impact, Notched 1/8" -30°C |
ASTM D256 | kg-cm/cm |
> 80 16 |
|
Hardness Shore D Hardness Rockwell R Scale |
ASTM D2240 ASTM D785 |
- | 72 |
| Thermal | |||
|
Heat Deflection Temperature (18.6kg/cm2 ) |
ASTM D648 | °C | 50 |
| Other | |||
| Shrinkage | ASTM D955 | % | 1.6~2.0 |
| Melt Index | ASTM D1238 | g/10min | > 5 |
| Specific Gravity | ASTM D792 | - | 1.07 |
| Ash Content | ASTM D482 | % | - |
| Equilibrium Moisture Content | ASTM D570 | % | < 0.3 |
| Flammability | UL 94 | 1.6mm | - |
2. Molding Condition:
| Drying | Melt Temp | Inject Press. |
|---|---|---|
| 80~100°C*4HR | 235~260°C | 20kg/cm2 |
Note: Test Conditions: 23℃, 50%RH, 24 hours. The datasheet is for your reference. And the data above will vary as the actual use condition changes.