PA6
Mineral Fiber Reinforced Grade
Mineral fiber reinforced nylon for superior strength, dimensional stability, and reduced warpage.
GRS certified. Providing high-performance customized modification services. Available in black, natural, and with custom coloring services.
Flexural modulus of 45,000–47,000 kg/cm², low warpage, and excellent dimensional stability. Great for automobile parts with low warpage or where paint plating is required.
Positioning: Materials requiring precise dimensional control (high flatness requirements).
Solveing deformation issues and improves product yield.
It can be applied to various product manufacturing, such as headlight base, bumper brackets, painted and plated appearance parts, engine peripheral structural components.
A3000M33BK
Material：
PA6
Specification：
33% mineral reinforcement
Color：
Black
Certification：
RoHS、REACH、GRS(Global Recycle Standard)
Package：
25kg
Property：
Excellent stiffness, strength and low warpage, suitable for electroplating processing characteristics
1. Materials Standard:
| Test Items Property | Test Method | Unit | Vaule |
|---|---|---|---|
| Mechanical Properties | |||
| Tensile Strength | ASTM D638 | Kg/cm2 | 750 |
| Elongation at Break | ASTM D638 | % | < 5 |
| Flexural Strength | ASTM D790 | kg/cm2 | 1200 |
| Flexural Modulus | ASTM D790 | kg/cm2 | 46000 |
|
IZOD Impact, Notched 1/8" 23°C IZOD Impact, Notched 1/8" -30°C |
ASTM D256 | kg-cm/cm |
4 |
|
Hardness Shore D Hardness Rockwell R Scale |
ASTM D2240 ASTM D785 |
- |
115 |
| Thermal | |||
|
Heat Deflection Temperature (18.6kg/cm2 ) |
ASTM D648 | °C | 200 |
| Other | |||
| Shrinkage | ASTM D955 | % | 0.2~0.8 |
| Melt Index | ASTM D1238 | g/10min | - |
| Specific Gravity | ASTM D792 | - | 1.39 |
| Ash Content | ASTM D482 | % | 33 |
| Equilibrium Moisture Content | ASTM D570 | % | < 0.3 |
| Flammability | UL 94 | 1.6mm | - |
2. Molding Condition:
| Drying | Melt Temp | Inject Press. |
|---|---|---|
| 80~100°C*4HR | 235~260°C | 20kg/cm2 |
Note: Test Conditions: 23℃, 50%RH, 24 hours. The datasheet is for your reference. And the data above will vary as the actual use condition changes.