PA6
Ultra Impact Modified Grade
Increase the toughness of nylon at low temperatures.
Our ultra impact modified PA6 is a grade to improve its impact resistance, it can increase the toughness of nylon at low temperatures.
It can apply on different product production such as: medical equipment, office chair caster, baby stroller accessories, sporting goods, suitscase wheel and more.
A2000TSDA3
Material：
PA6
Specification：
Low Temperature Impact Resistance
Color：
Natural color, providing custom dyeing service
Certification：
RoHS、REACH、GRS(Global Recycle Standard)
Package：
25kg
Property：
Excellent high toughness, low temperature impact resistance and surface improved
1. Materials Standard:
| Test Items Property | Test Method | Unit | Vaule |
|---|---|---|---|
| Mechanical Properties | |||
| Tensile Strength | ASTM D638 | Kg/cm2 | 430 |
| Elongation at Break | ASTM D638 | % | > 70 |
| Flexural Strength | ASTM D790 | kg/cm2 | 700 |
| Flexural Modulus | ASTM D790 | kg/cm2 | 16000 |
|
IZOD Impact, Notched 1/8" 23°C IZOD Impact, Notched 1/8" -30°C |
ASTM D256 | kg-cm/cm |
> 85 16 |
|
Hardness Shore D Hardness Rockwell R Scale |
ASTM D2240 ASTM D785 |
- | 72 |
| Thermal | |||
|
Heat Deflection Temperature (18.6kg/cm2 ) |
ASTM D648 | °C | 50 |
| Other | |||
| Shrinkage | ASTM D955 | % | 1.6~2.0 |
| Melt Index | ASTM D1238 | g/10min | > 15 |
| Specific Gravity | ASTM D792 | - | 1.07 |
| Ash Content | ASTM D482 | % | - |
| Equilibrium Moisture Content | ASTM D570 | % | < 0.3 |
| Flammability | UL 94 | 1.6mm | - |
2. Molding Condition:
| Drying | Melt Temp | Inject Press. |
|---|---|---|
| 80~100°C*4HR | 235~260°C | 20kg/cm2 |
Note: Test Conditions: 23℃, 50%RH, 24 hours. The datasheet is for your reference. And the data above will vary as the actual use condition changes.
A2000TSDG2
Material：
PA6
Specification：
Low Temperature Impact Resistance
Color：
Natural color, providing custom dyeing service
Certification：
RoHS、REACH、GRS(Global Recycle Standard)
Package：
25kg
Property：
Excellent high toughness and stiffness, low temperature impact resistance and surface improved
1. Materials Standard:
| Property | Test Method | Unit | Vaule |
|---|---|---|---|
| Mechanical Properties | |||
| Tensile Strength | ASTM D638 | Kg/cm2 | 500 |
| Elongation at Break | ASTM D638 | % | > 70 |
| Flexural Strength | ASTM D790 | kg/cm2 | 800 |
| Flexural Modulus | ASTM D790 | kg/cm2 | 19000 |
|
IZOD Impact, Notched 1/8" 23°C IZOD Impact, Notched 1/8" -30°C |
ASTM D256 | kg-cm/cm |
> 85 10 |
|
Hardness Shore D Hardness Rockwell R Scale |
ASTM D2240 ASTM D785 |
- | 72 |
| Thermal | |||
|
Heat Deflection Temperature (18.6kg/cm2 ) |
ASTM D648 | °C | 50 |
| Other | |||
| Shrinkage | ASTM D955 | % | 1.6~2.0 |
| Melt Index | ASTM D1238 | g/10min | > 15 |
| Specific Gravity | ASTM D792 | - | 1.08 |
| Ash Content | ASTM D482 | % | - |
| Equilibrium Moisture Content | ASTM D570 | % | < 0.3 |
| Flammability | UL 94 | 1.6mm | - |
2. Molding Condition:
| Drying | Melt Temp | Inject Press. |
|---|---|---|
| 80~100°C*4HR | 235~260°C | 20kg/cm2 |
Note: Test Conditions: 23℃, 50%RH, 24 hours. The datasheet is for your reference. And the data above will vary as the actual use condition changes.
A3501TBKA2
Material：
PA6
Specification：
Low Temperature Impact Resistance
Color：
Black
Certification：
RoHS、REACH、GRS(Global Recycle Standard)
Package：
25kg
Property：
Excellent high toughness and stiffness, low temperature impact resistance and surface improved
1. Materials Standard:
| Property | Test Method | Unit | Vaule |
|---|---|---|---|
| Mechanical Properties | |||
| Tensile Strength | ASTM D638 | Kg/cm2 | 500 |
| Elongation at Break | ASTM D638 | % | > 20 |
| Flexural Strength | ASTM D790 | kg/cm2 | 850 |
| Flexural Modulus | ASTM D790 | kg/cm2 | 20000 |
|
IZOD Impact, Notched 1/8" 23°C IZOD Impact, Notched 1/8" -30°C |
ASTM D256 | kg-cm/cm |
> 10 5 |
|
Hardness Shore D Hardness Rockwell R Scale |
ASTM D2240 ASTM D785 |
- | 72 |
| Thermal | |||
|
Heat Deflection Temperature (18.6kg/cm2 ) |
ASTM D648 | °C | 50 |
| Other | |||
| Shrinkage | ASTM D955 | % | 1.6~2.0 |
| Melt Index | ASTM D1238 | g/10min | > 50 |
| Specific Gravity | ASTM D792 | - | 1.10 |
| Ash Content | ASTM D482 | % | - |
| Equilibrium Moisture Content | ASTM D570 | % | < 0.3 |
| Flammability | UL 94 | 1.6mm | - |
2. Molding Condition:
| Drying | Melt Temp | Inject Press. |
|---|---|---|
| 80~100°C*4HR | 235~260°C | 20kg/cm2 |
Note: Test Conditions: 23℃, 50%RH, 24 hours. The datasheet is for your reference. And the data above will vary as the actual use condition changes.
A3000TBKA3
Material：
PA6
Specification：
Low Temperature Impact Resistance
Color：
Black
Certification：
RoHS、REACH、GRS(Global Recycle Standard)
Package：
25kg
Property：
Excellent high toughness, low temperature impact resistance and surface improved
1. Materials Standard:
| Property | Test Method | Unit | Vaule |
|---|---|---|---|
| Mechanical Properties | |||
| Tensile Strength | ASTM D638 | Kg/cm2 | 430 |
| Elongation at Break | ASTM D638 | % | > 50 |
| Flexural Strength | ASTM D790 | kg/cm2 | 700 |
| Flexural Modulus | ASTM D790 | kg/cm2 | 17500 |
|
IZOD Impact, Notched 1/8" 23°C IZOD Impact, Notched 1/8" -30°C |
ASTM D256 | kg-cm/cm |
> 80 16 |
|
Hardness Shore D Hardness Rockwell R Scale |
ASTM D2240 ASTM D785 |
- | 72 |
| Thermal | |||
|
Heat Deflection Temperature (18.6kg/cm2 ) |
ASTM D648 | °C | 50 |
| Other | |||
| Shrinkage | ASTM D955 | % | 1.6~2.0 |
| Melt Index | ASTM D1238 | g/10min | > 20 |
| Specific Gravity | ASTM D792 | - | 1.07 |
| Ash Content | ASTM D482 | % | - |
| Equilibrium Moisture Content | ASTM D570 | % | < 0.3 |
| Flammability | UL 94 | 1.6mm | - |
2. Molding Condition:
| Drying | Melt Temp | Inject Press. |
|---|---|---|
| 80~100°C*4HR | 235~260°C | 20kg/cm2 |
Note: Test Conditions: 23℃, 50%RH, 24 hours. The datasheet is for your reference. And the data above will vary as the actual use condition changes.